Copper-zinc alloys are difficult to prepare because they have a tendency to smear easily. The result is preparation damage and scratching may only become apparent after etching.
SECTIONING
MAXCUT Abrasive blade (Cat. No. MAX-C or MAX-I series)
MOUNTING
Compression Mounting with Phenolic, Epoxy or Diallyl Phthalate compression mounting resins
POLISHING
Abrasive/surface |
Lubricant |
Force/ sample |
Speed |
Time |
P220 grit ALO paper |
Water |
5-10 lbs |
100/100 rpm |
Until plane |
1 um DIAMAT diamond on ATLANTIS polishing pad |
DIALUBE Purple Extender |
5-10 lbs |
100/100 rpm |
2 minutes |
0.05 um Nanometer alumina on NAPPAD polishing pad |
|
5-10 lbs |
100/100 rpm |
1 minute |
 |
Copper-Zinc alloy, 200X |